Nhan đề: Characterization of hydroxyapatite/carbon nanotubes coatings on Ti6AI4V
Tác giả: Nguyen, Thi Thom
Pham, Thi Nam
Nguyen, Van Trang
Nguyen, Tuan Anh
Pham, Tien Dung
Dinh, Thi Mai Thanh
Từ khoá: Hydroxyapatite
HAp/CNTs coatings
Ti6A14V
Electrodeposition
Năm xuất bản: 2018
Tùng thư/Số báo cáo: Vietnam Journal of Chemistry;Vol. 56, No. 05 .- P.602-605
Tóm tắt: Carbon nanotubes (CNTs) possess excellent mechanical properties for their role playing in reinforcement as imparting strength to hydroxyapatite (HAp) coating. This work reports the electrodeposition of HAp/CNTs coatings on Ti6A14V substrate at scanning potentials range of (H-2.0 V/SCE, 5 mV/s, 5 scans at 45°C with the different functionalized CNTs concentration. The characterizations of the coatings were investigated. The amount of functionalized CNTs was determined using thermal gravimetric analysis. The X-ray diffraction results showed that HAp/CNTs nanocomposite coatings were composed of HAp and CNTs. The diffraction peak with the highest intensity found at 20 about 32° corresponding to the (2 11) HAp crystal and the peak at 26.3° can be assigned to (0 0 2) plane of CNTs. The HRTEM image confirmed the presence of CNTs in the coatings and CNTs amount of 7.25 % by TGA result.
Định danh: https://dspace.ctu.edu.vn/jspui/handle/123456789/40850
ISSN: 2525-2321
Bộ sưu tập: Vietnam Journal of Chemistry

Các tập tin trong tài liệu này:
Tập tin Mô tả Kích thước Định dạng  
_file_
  Giới hạn truy cập
1.3 MBAdobe PDF
Your IP: 44.197.114.92


Khi sử dụng các tài liệu trong Thư viện số phải tuân thủ Luật bản quyền.