Nhan đề: | Preparation and corrosion protection of polypyrrole/SiO₂ nanocomposite doped with 3-nitrosalicylic acid on aluminum |
Tác giả: | Le, Van Khoe Ha, Manh Hung Hoang, Thi Thuy Pham, Huy Binh Bui, Tuan Anh Le, Minh Duc Nguyen, Thi Huong Doan, Thi Yen Oanh Nguyen, Xuan Thai Vu, Quoc Trung |
Từ khoá: | 3-nitrosalicylic acid Aluminum Corrosion protection Nanocomposite Polypyrrole Self-healing |
Năm xuất bản: | 2024 |
Tùng thư/Số báo cáo: | Vietnam journal of Chemitry;Vol.62, Iss.04 .- P.540-546 |
Tóm tắt: | Polypyrrole/SiO₂ nanocomposite doped with 3-nitrosalicylic acid was synthesized in three concentrations of 3-nitrosalicylic acid: 0.01 M, 0.005 M, and 0.0025 м. FTIR spectroscopy, thermogravimetric analysis (TGA), Raman scattering spectroscopy, and FESEM imaging further assisted in determining the shape and structure of the polypyrrole/nanocomposite product. The aluminum protection arrangement of the paint film comprising polypyrrole/SiO₂ nanocomposite doped with 3-nitrosalicylic acid was proven by electrochemical methods. The salt spray test results also demonstrated the protective efficacy of the paint film comprising polypyrrole/SiO₂ nanocomposite doped with 3-nitrosalicylic acid to suppress corrosion. The best corrosion prevention results were obtained with a polypyrrole/SiO₂ nanocomposite dispersion paint film doped with 0.01 м 3-nitrosalicylic acid at a concentration of 2%. |
Định danh: | https://dspace.ctu.edu.vn/jspui/handle/123456789/109364 |
ISSN: | 2525-2321 |
Bộ sưu tập: | Vietnam Journal of Chemistry |
Các tập tin trong tài liệu này:
Tập tin | Mô tả | Kích thước | Định dạng | |
---|---|---|---|---|
_file_ Giới hạn truy cập | 2.45 MB | Adobe PDF | ||
Your IP: 3.138.101.51 |
Khi sử dụng các tài liệu trong Thư viện số phải tuân thủ Luật bản quyền.