Nhan đề: | Fabrication and property characterization of biocomposite based on polyamide 11 and AP1 green ramie fiber modified with epoxy |
Tác giả: | Dam, Xuan Thang Tran, Thi Mai Nguyen, Vu Giang Mai, Duc Huynh Tran, Huu Trung Nguyen, Thi Thu Trang Nguyen, Huu Dat Do, Van Cong Luong, Nhu Hai Thai, Hoang |
Từ khoá: | Bio-composites Epoxy Mechanical aroperties Polyamide 11 Ramie fiber |
Năm xuất bản: | 2024 |
Tùng thư/Số báo cáo: | Vietnam journal of Chemistry;Vol.62, Iss.05 .- P.647-656 |
Tóm tắt: | In this article, Vietnam ramie fiber from Moc Chau, Son La province was chosen as a reinforcement for polyamide 11 (PA11) to prepare full biocomposites. To enhance the compatibility and adhesion with the matrix, the original ramie fiber (ORF) was treated with Ca(OH), solution (tRF) and then modified by epoxy (mRF). Properties and structure of these fibers were characterized by tensile test, chemical composition, Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). The obtained results showed the removal of hemicellulose and lignin after treatment improved the morphology and mechanical properties of the fiber. Rheology in melting state indicated the increase in the torque of PA11 matrix by adding tRF and mRF. The improvement in mechanical properties was observed for both PA11/tRF and PA11/mRF composites. After modification, epoxy on the fiber surface enhanced the adhesion and compatibility with the matrix. This led to a strong increase in Young's modulus. tensile strength and flexural strength of about 37%, 57%, and 33%, respectively. TRF and mRF also improved thermal stability of the composite as shown in TGA and DSC analysis. Finally, mRF showed a better compatibility with PA11 than tRF by observation of SEM images. |
Định danh: | https://dspace.ctu.edu.vn/jspui/handle/123456789/109442 |
ISSN: | 2525-2321 |
Bộ sưu tập: | Vietnam Journal of Chemistry |
Các tập tin trong tài liệu này:
Tập tin | Mô tả | Kích thước | Định dạng | |
---|---|---|---|---|
_file_ Giới hạn truy cập | 3.72 MB | Adobe PDF | ||
Your IP: 18.119.19.206 |
Khi sử dụng các tài liệu trong Thư viện số phải tuân thủ Luật bản quyền.