Nhan đề: Application of modified kaolinite in improving thermal stability of polydimethylsiloxane
Tác giả: Nguyen, Linh T. T.
No, Kwangsoo
Jiang, Zhong-Tao
Liew, Willey Yun Hsien
Mondinos, Nicholas
Phan, Tuan D.
Từ khoá: Hydrogenated tallow amine
Intercalation
Kaolinite
Polydimethylsiloxane
Thermal stability
Năm xuất bản: 2024
Tùng thư/Số báo cáo: Vietnam Journal of Chemistry;Vol.62, Iss.05 .- P.697-703
Tóm tắt: This research investigated the chemical structure and morphology of the hydrogenated tallow amine (HTA)‐intercalated kaolinite by XRD, FT‐IR, and TEM measurements. The experimental outcomes show that intercalation of kaolinite by HTA, with an intercalation rate of 63.2%, expands the interlayer distance with a subsequent dominant basal XRD peak at 2 θ ≈ 7.9°. Furthermore, a composite was created from the HTA‐intercalated kaolinite and polydimethylsiloxane (PDMS) through a favorable interaction between the end silanol groups of PDMS and the modified kaolinite surface. Thermogravimetry‐differential scanning calorimetry results indicate that introducing the HTA‐intercalated kaolinite into the PDMS matrix increases the thermal stability of the composite from 178 to 343°C. However, the thermal stability of the composite is lower than that of other published materials. The synthesis of kaolinite/PDMS composite with enhanced structural and thermal stability outcomes has been provided via a simple and effective solution method that should have further applications.
Định danh: https://dspace.ctu.edu.vn/jspui/handle/123456789/109491
ISSN: 2525-2321
Bộ sưu tập: Vietnam Journal of Chemistry

Các tập tin trong tài liệu này:
Tập tin Mô tả Kích thước Định dạng  
_file_
  Giới hạn truy cập
2.52 MBAdobe PDF
Your IP: 18.223.238.150


Khi sử dụng các tài liệu trong Thư viện số phải tuân thủ Luật bản quyền.