Nhan đề: Nanosilica from canary seed husk for corrosion protection of structural steel
Tác giả: Sliva, U. León
Nicho, M. E.
Sotelo, L. Cajero
Guerrero, C. F. Castro
Alatorre, Jesús Escobedo
Guillén, M. R. Díaz
Từ khoá: Canary sood husk
Corrosion
Nanosilica
Steel
Surface treatment
Năm xuất bản: 2024
Tùng thư/Số báo cáo: Vietnam Journal of Chemistry;Vol.62, Iss.05 .- P.717-726
Tóm tắt: An alternative technique is presented for the corrosion protection of the A36 structural steel (A3655) in acid medium (H₂SO₄) using silica obtained from canary seed nusk (CSH). The silica was obtained in a solid amorphous state with a particle size of 10-22 nm. The anticorrosive properties of nanosilica (NS) were studied using potentiodynamic polarization (PDP), linear polarization resistance (LPR), and electrochemical impedance spectroscopy (EIS), Before carrying out the corrosion tests, the A36SS was subjected to a treatment with NaOH selution without and with the presence of NS. The A3555 treated with NS presented the lowest current density values and the noblest corrosion potential values, indicating that the corrosion rate decreased. The surface morphological study of the tested systems. using SEM/EDS showed that the NS-treated A36SS had a more efficient physical barrier against corrosive species.
Định danh: https://dspace.ctu.edu.vn/jspui/handle/123456789/109495
ISSN: 2525-2321
Bộ sưu tập: Vietnam Journal of Chemistry

Các tập tin trong tài liệu này:
Tập tin Mô tả Kích thước Định dạng  
_file_
  Giới hạn truy cập
3.66 MBAdobe PDF
Your IP: 3.137.200.56


Khi sử dụng các tài liệu trong Thư viện số phải tuân thủ Luật bản quyền.