Nhan đề: Effect of sodium hydroxide treatment on the fracture toughness of luffa natural fiber reinforced epoxy epikote 828
Tác giả: Dang, Huu Trung
Doan, Thi Yen Oanh
Từ khoá: Opoxy resin
Fracture toughness
Lufla natural fiber
Socium hydroxide treatment
Năm xuất bản: 2024
Tùng thư/Số báo cáo: Vietnam journal of Chemistry;Vol.62, Iss.05 .- P.727-735
Tóm tắt: Microsized luffa natural fibers (MLNFs) were derived from raw luffa natural fibers from Vietnam by undergoing treatment with sodium hydroxide. This study examined the impact of sodium hydroxide concentration, temperature, and treatment duration on the fracture toughness of epoxy resin 828 reinforced with MLNFS. The results showed that the fracture toughness of the composite, as measured by the critical-stress-intensity factor (K) and Izod impact strength, was improved after the treatment of the MLNFs with sodium hydroxide. Specifically, with the optimal sodium hydroxide treatment parameters of 6% NaOH at 70 °C for 6 h, the critical-stressintensity factor increased by 93% (from 2.0 to 3.86 MPa m2) and the Izod impact strength rose by 44.6% (from 3.81 το 5.51 kJ/m²). The thermal properties and surface structure of MLNFs treated with NaOH were analyzed using thermogravimetric analysis (TGA) and scanning electron microscopy (SEM) images.
Định danh: https://dspace.ctu.edu.vn/jspui/handle/123456789/109498
ISSN: 2525-2321
Bộ sưu tập: Vietnam Journal of Chemistry

Các tập tin trong tài liệu này:
Tập tin Mô tả Kích thước Định dạng  
_file_
  Giới hạn truy cập
3.35 MBAdobe PDF
Your IP: 52.14.204.52


Khi sử dụng các tài liệu trong Thư viện số phải tuân thủ Luật bản quyền.