Title: Preparation of rod-like MgO by simple precipitation method for CO₂ capture at ambient temperature
Authors: Vu, Anh Tuan
Lee, Chang Ha
Keywords: MgO
Rod-like
Carbon dioxide
Capture
Regeneration
Issue Date: 2018
Series/Report no.: Vietnam Journal of Chemistry;No 02 .- Page.197-202
Abstract: Rod-like MgO was prepared by the simple precipitation method and subsequenitly evaluated for CO₂ capture efficiency under ambient-tempcrature adsorption and intermediate-temperature regeneration. The MgO precursor was analyzed by thermogravimetric analysis (TGA) and X-ray power diffraction (XRD), it was decomposed completely at 500 °C to form MgO. The as-synthesized MgO samples were characterized by XRD, BET and PE-SEM. The MgO samples were comprised of grains with an approximate length of 4-6 µm and diameter of 0.5 µm. The BET surface area of MgO was 330.5 m²/g, which was much higher than that of commercial MgO (CM-MgO, 103.2 m²/g). The CO₂ uptake on MgO samples were evaluated by TGA. As-synthesized MzO had the high CO₂ sorption capacity compared to CM-MgO. The effect of temperature on CO₂ sorption capacity was also investigated. In addition, the stability of sample was evaluated by cyclic experiment.
URI: http://dspace.ctu.edu.vn/jspui/handle/123456789/21704
ISSN: 2525-2321
Appears in Collections:Vietnam Journal of Chemistry

Files in This Item:
File Description SizeFormat 
_file_
  Restricted Access
4.32 MBAdobe PDF
Your IP: 3.144.104.175


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.