Nhan đề: Synthesis of bimetallic Cu-Ag nanoparticles prepared by DC high voltage electrochemical method
Tác giả: Nguyen, Duc Hung
Tran, Van Cong
Hoang, Nhu Trang
Từ khoá: Cu/Ag bimetallic
Nanopartieles
DC voltage
Silver
Copper
Năm xuất bản: 2019
Tùng thư/Số báo cáo: Vietnam Journal of Chemistry;Số 57(05) .- Tr.609-614
Tóm tắt: Copper-silver bimetallic nanoparticles (NPs) can be prepared by electrochemical high voltage DC using silver and copper anodes in double distilled water. Bimetallic nano formation of Cu-Ag-NPs were performed by dissolving the Ag anode in anodic dissolved Cu solution or in the Cu NPs solution. The dependence of the DC current and the amount of electricity on the time show the reaction with a 200 mm electrode gap with formation of electronic plasma. The product obtained at 5 kv had the same characteristics as AgNPs with UV-Vis spectrum: 420 nm, particle size distribution was mainly in small areas of 100 nm, zeta potential had value up to -80.6 mV as well as the good ability to kill bacteria.
Định danh: http://dspace.ctu.edu.vn/jspui/handle/123456789/25389
ISSN: 2525-2321
Bộ sưu tập: Vietnam Journal of Chemistry

Các tập tin trong tài liệu này:
Tập tin Mô tả Kích thước Định dạng  
_file_
  Giới hạn truy cập
1.04 MBAdobe PDF
Your IP: 18.225.56.181


Khi sử dụng các tài liệu trong Thư viện số phải tuân thủ Luật bản quyền.