Title: Research on fabrication of non-calcined geopolymer ceramics from kaolin Tung Ba, Vi Xuyen, Ha Giang
Authors: Tran, Thi Lan
Nguyen, Anh Duong
Tran, Thi Man
Keywords: Kaolin
Metakaolin
Geopolymer
Ceramic
Alkaline activator
Issue Date: 2019
Series/Report no.: Vietnam Journal of Earth Sciences;Vol. 41, No. 04 .- P.388–402
Abstract: The mineral component of kaolin clay in Tung Ba commune analyzed by X-ray diffraction is composed mainly of kaolinite (24–27%), illite (26–30%) and quartz (40–44%). Chemical composition (wt%) of Tung Ba kaolin determined by X-ray fluorescence (XRF) shows SiO₂ at 59.92–64.98, Al₂O₃: 18.95–20.82, Fe₂O₃: 2.28–3.95, SO₃: 2.47–4.66, CaO: 0.12–0.36, MgO: 1.72–2.13 and TiO₂ at 0.75–1,08. To fabricate geopolymer ceramic, kaolin clay was transformed into metakaolin with the optimal parameters of calcination: the temperature at 750°C and heating time of 120 min. Obtained metakaolin is mixed with mixtures of NaOH/Na₂SiO₃ (40%wt) with ratios of 0.2, 0.25, 0.33, 0.5 and NaOH molarities are 10M, 12M, 14M. Testing geopolymer ceramics after 28 days had a compressive strength of 40–196 KG/cm², water absorption of 15.25–17.98% and density of 1.54–1.69 g/cm³, totally satisfied the Vietnamese standard for construction bricks and ceramics.
URI: https://dspace.ctu.edu.vn/jspui/handle/123456789/67217
ISSN: 0866-7187
Appears in Collections:Vietnam journal of Earth sciences

Files in This Item:
File Description SizeFormat 
_file_
  Restricted Access
16.8 MBAdobe PDF
Your IP: 18.219.44.171


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.